PENGUJIAN KERETAKAN HASIL PENGELASAN SMAW DENGAN ALAT UJI BENDING TEST DAN DYE PENETRANT PADA BEBERAPA TIPE SAMBUNGAN LAS

NOFIYANTO HERMAWAN, . (2014) PENGUJIAN KERETAKAN HASIL PENGELASAN SMAW DENGAN ALAT UJI BENDING TEST DAN DYE PENETRANT PADA BEBERAPA TIPE SAMBUNGAN LAS. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text A1.COVER.pdf Download (107kB)
	Text A4.ABSTRACT (INGGRIS).pdf Download (84kB)
	Text A4.ABSTRAK (INDONESIA).pdf Download (86kB)
	Text BAB I.pdf Download (142kB)
	Text BAB II.pdf Download (994kB)
	Text BAB III.pdf Download (1MB)
	Text BAB IV.pdf Download (346kB)
	Text BAB V.pdf Download (8kB)
	Text C1.DAFTAR PUSTAKA.pdf Download (82kB)

Abstract

Pengelasanmerupakan penyambungan duabahan atau lebih yang didasarkan padaprinsip-prinsipprosesdifusi,sehinggaterjadipenyatuan bagian bahan yang disambung. Kelebihan sambungan las adalah konstruksi ringan, dapat menahan kekuatan yang tinggi, mudah pelaksanaannya, serta cukup ekonomis. Namun kelemahan yang paling utama adalah terjadinya perubahan struktur mikro bahan yang dilas, sehingga terjadi perubahan sifat fisik maupun mekanis dari bahan yang dilas.setelahdilakukanpengelasanmaka dilakukanpengujianyaitu uji lengkung (bending test) dengan cara di lengkungkan untuk membuktikan bahwa penyambungan logam benar-benar homogen antara logam induk dan logamlas,selanjutnyadilakukanpengujiandengan cairanpenembus(dyepenetranttest)dengancaradilumuri cairan penembus untuk memastikanbahwa hasilpengelasanadalahbaikatautidakterdapatcacat permukaanbahkansetelahdilakuanujilengkung,sehingga dapatdisimpulkan bahwapengelasanSMAW sangatbaikuntukbahandenganketebalan6 mm. ******** Weldingis theconnectionof twoormorematerialsthat are basedonthe principles ofdiffusionprocesses, resulting in theunification ofthematerialsto be joined. Excessweld jointsarelightweightconstruction, canwithstandhighstrength, easyimplementation, andquiteeconomical. However,most majorweaknessis the change ofthe microstructure ofthe materialbeing welded, resulting inchanges inphysical andmechanicalpropertiesof thematerialbeing welded.after the welding is carried out testing the bend test (bending test) with arch way to prove that the connection is really homogeneous metal between the base metal and weld metal, further testing with a penetrating liquid (dye penetrant test) by means of penetrating fluid covered to ensure that the weld is good or no surface defects even after the bend test was done, so it can be concluded that it is very good for SMAW welding material with a thickness of 6 mm.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Syaripuddin, M.Pd. ; 2). Drs. H. Sopiyan
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Rima Safitri .
Date Deposited:	16 Apr 2021 02:55
Last Modified:	16 Apr 2021 02:55
URI:	http://repository.unj.ac.id/id/eprint/16002

Actions (login required)

View Item