PENGARUH JUMLAH LAPISAN PENGELASAN SMAW TERHADAP NILAI KEKERASAN VICKERS, KOROSI, DAN STRUKTUR MAKRO PADA BAJA KARBON RENDAH DENGAN MENGGUNAKAN ELEKTRODA HV 450

ALPI CAHYADI, . (2023) PENGARUH JUMLAH LAPISAN PENGELASAN SMAW TERHADAP NILAI KEKERASAN VICKERS, KOROSI, DAN STRUKTUR MAKRO PADA BAJA KARBON RENDAH DENGAN MENGGUNAKAN ELEKTRODA HV 450. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER (2) (1).pdf Download (1MB)
	Text BAB 1.pdf Download (357kB)
	Text BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (178kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (303kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (491kB) | Request a copy

Abstract

Penelitian ini membahas tentang pengaruh jumlah lapisan pengelasan SMAW terhadap nilai kekerasan Vickers, korosi, dan struktur makro pada baja karbon rendah dengan menggunakan elektroda HV 450. Dalam penelitian ini, baja karbon rendah dengan ketebalan 10 mm telah dilas dengan menggunakan elektroda HV 450 menggunakan teknik pengelasan SMAW dengan variasi jumlah lapisan pengelasan yaitu 1 lapis, 2 lapis, dan 3 lapis. Ketiga sampel variasi diuji dengan menggunakan metode uji kekerasan Vickers, uji korosi dengan elektrokimia dan metode mikroskop optik. Hasil penelitian menunjukkan bahwa jumlah lapisan pengelasan SMAW berpengaruh terhadap nilai kekerasan Vickers, tingkat korosi, dan struktur makro pada baja karbon rendah. Nilai kekerasan Vickers pada 1 lapis pengelasan lebih rendah dibandingkan 2 lapis dan 3 lapis, sedangkan tingkat korosi pada 3 lapis lebih rendah dibandingkan 1 lapis dan 2 lapis. ***** This research discusses the effect of the number of SMAW welding layers on the Vickers hardness value, corrosion, and macro structure of low carbon steel using HV 450 electrode. In this research, low carbon steel with a thickness of 10 mm was welded using HV 450 electrode using SMAW welding technique with a variation of the number of welding layers, namely 1 layer, 2 layers, and 3 layers. The three samples were tested using the Vickers hardness test method, electrochemical corrosion test, and optical microscope method. The results of the research show that the number of SMAW welding layers has an effect on the Vickers hardness value, corrosion level, and macro structure of low carbon steel. The Vickers hardness value in one welding layer is lower than two layers and three layers, while the corrosion level in three layers is lower than one layer and two layers.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Syaripudin, M.Pd. ; 2). Dr. Ferry Budhi Susetyo, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Users 19420 not found.
Date Deposited:	10 Sep 2023 23:46
Last Modified:	10 Sep 2023 23:46
URI:	http://repository.unj.ac.id/id/eprint/40431

Actions (login required)

View Item