SINTESIS SILIKA GEL TERMODIFIKASI 3-AMINOPROPILTRIETOKSISILAN (APTES) DARI BONGGOL JAGUNG UNTUK ADSORPSI LOGAM Ni(II) DALAM LARUTAN

NUR HANIFAH, . (2017) SINTESIS SILIKA GEL TERMODIFIKASI 3-AMINOPROPILTRIETOKSISILAN (APTES) DARI BONGGOL JAGUNG UNTUK ADSORPSI LOGAM Ni(II) DALAM LARUTAN. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

Text SKRIPSI-NUR HANIFAH-3325122143.pdf Download (2MB)

Abstract

Sintesis silika gel dari bonggol jagung menggunakan metode sol gel dan modifikasi dengan gugus 3-aminopropiltrietoksisilan telah berhasil dilakukan. Hasil SEM pada Silika GelAPTES menunjukkan morfologi materialnya berbentuk butiran dan hasil EDX menunjukkan komposisinya terdiri dari 46,83% Silika, 40,06 % Oksigen dan 13,10% Nitrogen. Berdasarkan hasil karakterisasi SAA, material Silika Gel-APTES memiliki luas permukaan sebesar 310,3329 m2 /g, memiliki pori yang beragam (mesopori dan mikropori) dan hasil analisis menggunakan metode BJH menunjukkan distribusi pori pada Silika GelAPTES merupakan mesopori dengan ukuran porinya sekitar 10,6 nm. Hasil karakterisasi FTIR silika gel termodifikasi APTES menunjukkan adanya adanya pita serapan khas dari gugus fungsi siloksan (=Si–O–Si=), silanol (=Si–OH) amina (NH2) dan rantai alifatik (-CH2). Proses adsorpsi terhadap ion logam Ni(II) menggunakan metode batch. Proses adsorpsi terhadap ion logam Ni(II) menggunakan Silika Gel-APTES berlangsung baik pada pH 6 dan waktu 30 menit. Kapasitas adsorpsi maksimum dari Silika Gel-APTES sebesar 63,29 mg/g. Proses adsorpsi mengikuti model isoterm adsorpsi Langmuir dengan nilai konstanta Langmuirnya sebesar 1,03 L/mg. Hasil menunjukkan Silika Gel-APTES dapat menjadi alternatif adsorben rendah biaya dalam penanganan limbah logam berat. The synthesis of silica gel from the corn cob using sol-gel method and modification with the 3-aminopropyltriethoxysilane group has been successfully performed. The SEM results on modified Silica Gel-APTES showed the morphology of the material is granular and the EDX results showed the composition consisted of 46.83% silica, 40.06% oxygen and 13.10% nitrogen. Based of the characterization of SAA, indicates the material of Silica Gel-APTES has a surface area of 310,3329 m2 /g, has various pores (mesoporous and microporous) and the result of the analysis using BJH method show the distribution pores of Silica Gel-APTES is mesoporous with a size pore of 10,6 nm. The results of the characterization FTIR showed a typical absorption of the siloxane functional groups (= Si-O-Si =), silanol (= Si-OH) amine (NH2) and aliphatic chain (-CH2). The adsorption process on Ni (II) metal ions was carried out in a batch system. The adsorption process on Ni (II) metal ions using Silica Gel-APTES takes place both at pH 6 and 30 minutes. The maximum adsorption capacity of Silica Gel-APTES was 63.29 mg/g. The adsorption process follows Langmuir's adsorption isotherm model with a Langmuir constant value of 1.03 L / mg. The results show the Gel Silica-APTES can be an alternative to low cost adsorbents.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Yusmaniar M.Si 2) Arif Rahman, M.Sc
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	sawung yudo
Date Deposited:	13 Apr 2022 01:29
Last Modified:	13 Apr 2022 01:29
URI:	http://repository.unj.ac.id/id/eprint/26392

Actions (login required)

View Item