LARA PERMATA SARI, . (2015) STUDI PENGARUH JUMLAH MOL ZINC ASETAT DYHIDRATE TERHADAP STRUKTUR KRISTAL DAN FOTOLUMINESEN LAPISAN TIPIS ZnO. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.
![]() |
Text
Skripsi Lara_Fisika 2011_3225111272.pdf Download (2MB) |
Abstract
Telah dilakukan penumbuhan lapisan tipis ZnO dengan Zn(CH3COO)2.2H2O sebagai prekursor dan air deionisasi sebagai pelarut. Lapisan ditumbuhkan di atas substrat Si(111) dengan metode Ultrasonic Spray Pyrolisis pada suhu tumbuh 450oC selama 10 menit. Variasi jumlah mol Zn(CH3COO)2.2H2O adalah 0,01 mol, 0,02 mol dan 0,03 mol. Pengaruh jumlah mol terhadap struktur, ukuran butir, parameter kisi pada lapisan tipis ZnO dikarakterisasi dengan menggunakan X-ray diffraction (XRD) dan karakteristik fotoluminesen lapisan tipis ZnO diuji dengan menggunakan spectrofluorophotometer. Hasil analisis difraksi sinar-X menunjukkan bahwa semua sampel memiliki struktur hexagonal wurtzit, besarnya ukuran butir sampel prekursor 0,01 mol; 0,02 mol dan 0,03 mol berturut-turut yaitu 46,7 nm, 45,6 nm dan 54,8 nm. Hasil spektrum fotoluminesen sampel menunjukan 2 pita: pertama yaitu pita emisi eksiton pada daerah UV tepat pada panjang gelombang 359 nm. Kedua dengan lebar pita pada cahaya tampak hijau pada kisaran panjang gelombang 518- 570 nm. Intensitas terbesar yaitu pada sampel 0,02 mol. Sehingga berdasarkan hasil penelitian ini maka lapisan tipis yang paling optimal yaitu lapisan dengan menggunakan jumlah mol prekursor 0,02 mol. ********* ZnO thin film with Zn(CH3COO)2.2H2O powder as precursor and deionized water as a solvent were grown on substrate Si(111) by using Ultrasonic Spray Pyrolisis methode has been carried out. The growth temperature of film is 450oC for 10 minutes. The variety of mol Zn(CH3COO)2.2H2O are 0,01 mol, 0,02 mol and 0,03 mol. The effect of molarity on structure, grain size, the lattice parameter on thin films ZnO were investigated by X-ray diffraction (XRD) and the photoluminescence (PL) characteristics of ZnO film were investigated by spectrofluorophotometer. The X-ray diffraction analysis revealed that all samples have hexagonal wurtzite structure, the grain size thin films respective are 46,7 nm, 45,6 nm-54 ,8 nm. The photoluminescence spectra of ZnO shows two bands: the first is an exciton emission band in the UV region centered at 359 nm. The second is an intense band in the green region between 518 and 570 nm. The maximum intensity on sample 0,02 mol. Thus based on this result show that the optimum thin film which used mol of precursor 0,02 mol.
Item Type: | Thesis (Sarjana) |
---|---|
Additional Information: | 1). Dr. Iwan Sugihartono M,Si. ; 2). Dr. Erfan Handoko M,Si. |
Subjects: | Sains > Fisika |
Divisions: | FMIPA > S1 Fisika |
Depositing User: | Users 8922 not found. |
Date Deposited: | 23 May 2022 03:54 |
Last Modified: | 03 Jun 2022 07:15 |
URI: | http://repository.unj.ac.id/id/eprint/28595 |
Actions (login required)
![]() |
View Item |