MODIFIKASI PERSEN BERAT POLIMETIL METAKRILAT TERHADAP HASIL KARAKTERISASI POLIMER KRISTAL CAIR PMMA-RM82 MENGGUNAKAN METODE UV-CURING

BRYAN VALENTINO, . (2022) MODIFIKASI PERSEN BERAT POLIMETIL METAKRILAT TERHADAP HASIL KARAKTERISASI POLIMER KRISTAL CAIR PMMA-RM82 MENGGUNAKAN METODE UV-CURING. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (213kB)
	Text BAB 2.pdf Restricted to Registered users only Download (879kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (159kB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (157kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (4MB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Polimer kristal cair PMMA-RM82 telah berhasil disintesis dengan metode UV Curing. Penelitian ini dilakukan dengan menvariasikan persen berat PMMA yaitu 0%, 5%, 10%, 20%, dan 30% terhadap mesogen reaktif RM82 30%. Dari penelitian ini didapatkan beberapa informasi karakterisasi sampel seperti gugus fungsi, morfologi permukaan, perubahan kalor serta fasa yang terbentuk pada sampel. Pada pengujian dengan DSC dihasilkan pergeseran puncak endotermik dan eksotermik ke suhu yang lebih kecil seiring dengan bertambahnya persen berat PMMA. Kemudian pengujian sampel dengan FTIR didapatkan spektrum-spektrum yang memiliki kemiripan bentuk tetapi dengan pergeseran puncak pada setiap penambahan persen berat PMMA. Selanjutnya dilakukan pengujian dengan SEM didapatkan informasi perubahan bentuk permukaan sampel dari kristal berserat mirip bilah milik RM82, menjadi kristal serat dengan bulatan di ujung pada penambahan PMMA 5%, dan pada penambahan PMMA 30% menjadi bongkahan kristal. Pengujian terakhir pada sampel yaitu dengan XRD didapatkan puncak-puncak tajam yang terdapat pada 2θ di sekitar 10°, 20°, dan 21° yang menunjukkan semua sampel yang terbentuk memiliki fasa kristalin dan akan mengalami penurunan intensitas dengan meningkatnya persen berat PMMA. ****|| PMMA-RM82 liquid crystal polymer (LCP) has been successfully synthesized by UV Curing method. This research was conducted by varying the weight percent of PMMA, at 0%, 5%, 10%, 20%, and 30% towards reactive mesogen RM82 30%. This study achieved some characterization information of samples such as functional groups, surface morphology, heat changes and the phase-forming. In the DSC test, there is a shift of the endothermic and exothermic peaks to the lower temperature because of the PMMA’s weight percent increasity. Then the sample test with FTIR resulted in the similar spectrum peak but with a shift at each weight percent PMMA additional. Further testing with SEM recieved information of surface-shape transformation from the blade-like fibrous crystal belonging to RM82, to fiber crystals with spheres at the ends with the incorporation of 5% PMMA, and into crystal chunks form by the additional of 30% PMMA. The last test on the sample, is called XRD, obtained sharp peaks at 2θ at around 10°, 20°, and 21° which indicated that all the formed samples had a crystalline phase and would experience an intensity decreasing with increasing weight percent of PMMA.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dr. Afrizal, M.Si ; 2) Dr. Yusmaniar, M.Si
Subjects:	Sains > Kimia
Divisions:	FMIPA > S1 Kimia
Depositing User:	Users 16629 not found.
Date Deposited:	27 Oct 2022 01:43
Last Modified:	27 Oct 2022 01:43
URI:	http://repository.unj.ac.id/id/eprint/36602

Actions (login required)

View Item