PENGARUH VARIASI KOMPOSISI CAT TERHADAP KARAKTERISTIK COATING

USAMAH AHMAD MAULANA, . (2024) PENGARUH VARIASI KOMPOSISI CAT TERHADAP KARAKTERISTIK COATING. Diploma thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB I.pdf Download (1MB)
	Text BAB II.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (1MB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Baja ringan memiliki sifat kuat dan juga dapat digunakan dalam berbagai macam bidang industri. Baja SPCC memiliki kualitas yang lebih baik dari segi permukaan tetapi kekurangan dari baja ini yaitu sifat korosi. Upaya pencegahan dari korosi yaitu dengan pelapisan cat primer. Cat primer yang digunakan adalah polyurethane karena memiliki karakteristik anti gores, tahan lama, tidak mudah berjamur dan juga memiliki daya kilap tinggi. Cat polyurethane dibentuk melalui reaksi kimia antara polysocyanate dengan alkohol. Penelitian ini dilakukan untuk mengetahui pengaruh penambahan komposisi cat primer pada karakteristik lapisan cat (coating) menggunakan cat polyurethane terhadap ketebalan lapisan cat, daya lekat lekat cat dan juga melakukan pengujian bending untuk mengetahui keretakan pada hasil lapisan cat. Pada penelitian ini komposisi yang digunakan adalah cat, hardener, dan thinner dengan tiga variasi menggunakan perbandingan 5:1:2, 6:1:2, dan 7:1:2 dengan pengeringan pada suhu ruang antara 25-30oC selama 12 jam. Hasil yang diperoleh setelah pengujian menunjukkan hanya sedikit perbedaan yang didapatkan dari 3 variasi. Pada pengujian ketebalan hasil ketebalan tertinggi terdapat pada variasi 7:1:2 dengan nilai rata-rata ketebalan 62 μm. Pada pengujian daya lekat pada variasi 5:1:2 mendapatkan grade 5B, sedangkan 6:1:2 dan 7:1:2 mendapatkan hasil grade 4B dengan adanya cat yang terkelupas kurang dari 5% Pada hasil pengujian bending untuk 3 variasi yang di uji mendapatkan hasil yang sama dengan tidak adanya keretakan pada lapisan cat. Kata Kunci: baja SPCC, cat polyurethane, pengujian ketebalan. ***** Lightweight steel is strong and can be used in various fields of industry. SPCC steel has better surface quality, but its drawback is its susceptibility to corrosion. To prevent corrosion, a primer coating is applied. The primer used is polyurethane because it is scratch-resistant, durable, mold-resistant, and has a high gloss finish. Polyurethane paint is formed through a chemical reaction between polyisocyanate and alcohol. This research was conducted to determine the effect of varying primer compositions on the characteristics of the polyurethane coating, including coating thickness, adhesion, and to perform bending tests to observe cracks in the coating layer. The composition used in this study includes paint, hardener, and thinner with three variations in the ratios of 5:1:2, 6:1:2, and 7:1:2, with drying at room temperature between 25-30°C for 12 hours. The results showed only slight differences among the three variations. The highest thickness was observed in the 7:1:2 variation, with an average thickness of 62 microns. In the adhesion test, variation 5:1:2 achieved a grade of 5B, while the 6:1:2 and 7:1:2 variations received a grade of 4B, with less than 5% paint peeling. In the bending test results for the three variations tested, the outcomes were consistent, with no cracks observed in the paint layer.Adhesion testing showed that the 6:1:2 and 7:1:2 variations achieved a grade of 4B, with less than 5% of the paint peeling off. The bending test results for all three variations were identical, showing no cracks in the coating layer. Keywords: Polyurethane paint, SPCC steel, thick

Item Type:	Thesis (Diploma)
Additional Information:	1). Dr. Ferry Budhi Susetyo, M.T., M.Si. ; 2). Drs. Syamsuir, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Usamah Ahmad Maulana .
Date Deposited:	28 Jul 2024 23:30
Last Modified:	28 Jul 2024 23:30
URI:	http://repository.unj.ac.id/id/eprint/46999

Actions (login required)

View Item