ANALISIS PENGARUH TEMPERATUR CETAKAN SAMPAH PLASTIK HDPE (HIGH DENSITY POLYETHYLENE) TERHADAP KEKUATAN TARIK

ALFI DIFANZA, . (2024) ANALISIS PENGARUH TEMPERATUR CETAKAN SAMPAH PLASTIK HDPE (HIGH DENSITY POLYETHYLENE) TERHADAP KEKUATAN TARIK. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (2MB)
	Text BAB I.pdf Download (726kB)
	Text BAB II.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB III.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB IV.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB V.pdf Restricted to Registered users only Download (601kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (495kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Sampah plastik merupakan masalah global yang kompleks dan memerlukan solusi inovatif untuk mengurangi dampak lingkungannya. Plastik, yang terbagi menjadi beberapa jenis seperti PETE, HDPE, dan lainnya. Penelitian ini bertujuan menganalisis pengaruh variasi suhu cetakan terhadap kekuatan tarik produk plastik daur ulang, khususnya HDPE, menggunakan mesin press plastik. Metode penelitian yang digunakan adalah eksperimental kuantitatif dengan variasi suhu cetakan 110°C, 120°C, dan 130°C. Hasil penelitian menunjukkan bahwa suhu optimal untuk pembentukan HDPE adalah 130°C. Kekuatan tarik maksimum rata-rata tertinggi dicapai pada suhu 130°C sebesar 1821,8 N, sedangkan suhu 110°C menghasilkan kekuatan tarik terendah sebesar 1602,3 N. Dengan pemahaman ini, pengaturan suhu yang tepat dapat meningkatkan kualitas produk daur ulang plastik. Plastic waste is a complex global problem and requires innovative solutions to reduce its environmental impact. Plastic, which is divided into several types such as PETE, HDPE, and others. This research aims to analyze the effect of variations in mold temperature on the tensile strength of recycled plastic products, especially HDPE, using a plastic press machine. The research method used is quantitative experimental with variations in mold temperature of 110°C, 120°C and 130°C. The research results show that the optimal temperature for HDPE formation is 130°C. The highest average maximum tensile strength was achieved at a temperature of 120°C of 1821,8 N, while a temperature of 130°C produced the lowest tensile strength of 1602,3 N. With this understanding, setting the right temperature can improve the quality of plastic recycled products.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Eko Arif Saefuddin, M.T. 2). Ahmad Kholil, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Hidraulik, Pelabuhan, Irigasi Teknologi dan Ilmu Terapan > Teknik Lingkungan, Teknik Sanitasi Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Users 24094 not found.
Date Deposited:	02 Aug 2024 06:41
Last Modified:	02 Aug 2024 06:41
URI:	http://repository.unj.ac.id/id/eprint/48062

Actions (login required)

View Item