ANALISIS KEKERASAN PERMUKAAN BAJA KARBON RENDAH HASIL PROSES PENEMPAAN DAN QUENCHING

WISNU AL AMIN, . (2025) ANALISIS KEKERASAN PERMUKAAN BAJA KARBON RENDAH HASIL PROSES PENEMPAAN DAN QUENCHING. Diploma thesis, UNIVERSITAS NEGERI JAKARTA.

	Text File COVER.pdf Download (2MB)
	Text File BAB 1.pdf Download (303kB)
	Text File BAB 2.pdf Restricted to Registered users only Download (484kB) | Request a copy
	Text File BAB 3.pdf Restricted to Registered users only Download (668kB) | Request a copy
	Text File BAB 4.pdf Restricted to Registered users only Download (893kB) | Request a copy
	Text File BAB 5.pdf Restricted to Registered users only Download (297kB) | Request a copy
	Text File Daftar Pustaka.pdf Download (211kB)
	Text File Lampiran.pdf Restricted to Registered users only Download (341kB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengevaluasi perubahan sifat mekanik dan mikrostruktur pada spesimen besi setelah menjalani proses penempaan, yang melibatkan pemanasan menggunakan tungku tempa berbahan bakar gas LPG serta proses pendinginan (quenching) dengan berbagai jenis media. Pemanasan dilakukan hingga mencapai suhu 800°C, diikuti dengan pendinginan cepat menggunakan udara, minyak, oli, dan air sebagai media pendingin. Pengujian kekerasan dilakukan dengan metode Vickers, sedangkan analisis mikrostruktur dilakukan untuk mengidentifikasi perubahan fasa yang terjadi. Hasil menunjukkan bahwa jenis media pendingin memberikan pengaruh yang signifikan terhadap nilai kekerasan. Spesimen yang didinginkan menggunakan air menunjukkan nilai kekerasan tertinggi sebesar 374,8 VHN, pendingnan menggunakan minyak sebesar 259,2 VHN, dan pendinginan menggunakan oli sebesar 210,4 VHN, serta pendinginan menggunakan udara sebesar 190,0 VHN. Temuan ini menunjukkan bahwa pendinginan dengan media yang memiliki laju dingin tinggi, seperti air, cenderung menghasilkan struktur martensit yang lebih dominan, sehingga meningkatkan kekerasan material. Penelitian ini memberikan kontribusi terhadap pengembangan proses penempaan dan perlakuan panas untuk meningkatkan sifat mekanik logam, khususnya pada sektor industri kecil dan menengah. Kata kunci: penempaan, pendinginan cepat, kekerasan Vickers, tungku LPG, martensit. ***** This study aims to evaluate the changes in mechanical properties and microstructure of iron specimens after undergoing a forging process, which involves heating using an LPG gas-fueled forging furnace and a cooling process (quenching) with various types of media. Heating is carried out until it reaches a temperature of 800°C, followed by rapid cooling using air, oil, oil, and water as cooling media. Hardness testing is carried out using the Vickers method, while microstructural analysis is carried out to identify the phase changes that occur. The results show that the type of cooling media has a significant effect on the hardness value. Specimens cooled using water showed the highest hardness value of 374.8 VHN, using cooling oil 259.2 VHN, and using cooling oil 210.4 VHN, and using cooling water 190.0 VHN. These findings indicate that cooling with media that have a high cooling rate, such as water, tends to produce a more dominant martensite structure, thereby increasing the hardness of the material. This study contributes to the development of forging and heat treatment processes to improve the mechanical properties of metals, especially in the small and medium industrial sector. Keywords: forging, quenching, Vickers hardness, LPG furnace, martensite

Item Type:	Thesis (Diploma)
Additional Information:	1). Ahmad Lubi, M.Pd., M.T ; 2). Dr. Wardoyo, S.T., M.T.
Subjects:	Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Users 28969 not found.
Date Deposited:	12 Aug 2025 08:44
Last Modified:	12 Aug 2025 08:44
URI:	http://repository.unj.ac.id/id/eprint/59801

Actions (login required)

View Item