PENGARUH VARIASI KOMPOSISI FLY ASH, PERLITE, DAN TAMBAHAN POLYPROPYLENE FIBER TERHADAP KUAT TEKAN DAN GUGUS FUNGSI BETON GEOPOLIMER TIDAK DIBAKAR DAN DIBAKAR PADA TEMPERATUR 900°C

AHMAD FIKRI SYAIFUL, . (2025) PENGARUH VARIASI KOMPOSISI FLY ASH, PERLITE, DAN TAMBAHAN POLYPROPYLENE FIBER TERHADAP KUAT TEKAN DAN GUGUS FUNGSI BETON GEOPOLIMER TIDAK DIBAKAR DAN DIBAKAR PADA TEMPERATUR 900°C. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (321kB)
	Text BAB 2.pdf Restricted to Registered users only Download (635kB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (300kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (347kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Sistem proteksi kebakaran pada bangunan gedung berfungsi untuk mencegah kerusakan maupun kerugian akibat kebakaran melalui pembatasan penyebaran api dan asap, serta memberikan waktu evakuasi bagi penghuni. Umumnya, bangunan di Indonesia menggunakan semen portland sebagai bahan utama beton. Namun, proses produksinya menghasilkan 5–7% emisi CO₂ yang berdampak pada pemanasan global. Oleh karena itu, diperlukan inovasi material ramah lingkungan sebagai alternatif pengganti semen portland. Penelitian ini memanfaatkan fly ash dan perlite sebagai bahan utama karena kandungan silika dan alumina yang tinggi, dengan tambahan polypropylene fiber untuk meningkatkan sifat mekanik beton geopolimer. Larutan aktitator yang digunakan berupa NaOH dan Na₂SiO₃. Variasi komposisi beton geopolimer dibuat dalam lima rasio campuran fly ash dan perlite dengan polypropylene fiber tetap. Setiap variasi diuji pada dua kondisi, yaitu tanpa pembakaran dan setelah pembakaran pada suhu 900°C selama 2 jam. Pengujian meliputi kuat tekan menggunakan Compression Testing Machine (CTM) dan karakterisasi gugus fungsi dengan Fourier Transform Infrared (FTIR). Hasil penelitian menunjukkan bahwa komposisi 2 dengan rasio fly ash 75% dan perlite 25% ditambah polypropylene fiber menghasilkan sifat paling optimal dibandingkan variasi lainnya. Komposisi ini memiliki kuat tekan lebih baik serta struktur ikatan yang lebih stabil berdasarkan analisis FTIR, sehingga berpotensi menjadi alternatif material beton ramah lingkungan dengan ketahanan yang baik terhadap suhu tinggi. ***** The fire protection system in buildings functions to prevent damage and losses caused by fire by limiting the spread of flames and smoke, while also providing sufficient evacuation time for occupants. In Indonesia, Portland cement is commonly used as the main binder in concrete structures. However, its production generates 5–7% CO₂ emissions, contributing to global warming. Therefore, eco-friendly materials are needed as alternatives to Portland cement. This study utilized fly ash and perlite as the main materials due to their high silica and alumina content, with the addition of polypropylene fiber to improve the mechanical properties of geopolymer concrete. The alkaline activator solution consisted of NaOH and Na₂SiO₃. Five variations of fly ash–perlite mixtures with constant polypropylene fiber content were prepared. Each composition was tested under two conditions: without burning and after burning at 900°C for 2 hours. The tests included compressive strength measurement using a Compression Testing Machine (CTM) and functional group characterization using Fourier Transform Infrared (FTIR). The results indicated that composition 2, with 75% fly ash and 25% perlite combined with polypropylene fiber, produced the most optimal performance compared to other variations. This composition exhibited higher compressive strength and more stable bonding structure as confirmed by FTIR analysis, demonstrating its potential as an environmentally friendly alternative material for concrete with good resistance to high temperatures.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Fransisca Maria Farida, S.T., M.T. ; 2). Dr. Hanhan Dianhar, M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil Teknologi dan Ilmu Terapan > Konstruksi Bangunan
Divisions:	FT > S1 Rekayasa Keselamatan Kebakaran
Depositing User:	Users 31690 not found.
Date Deposited:	17 Oct 2025 03:14
Last Modified:	17 Oct 2025 03:14
URI:	http://repository.unj.ac.id/id/eprint/62701

Actions (login required)

View Item