PENGARUH PENAMBAHAN UNSUR MAGNESIUM (Mg) TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK LOGAM ZINC (Zn) UNTUK APLIKASI MATERIAL IMPLAN ORTOPEDI

RADITE TEDYA FAIZY, . (2025) PENGARUH PENAMBAHAN UNSUR MAGNESIUM (Mg) TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK LOGAM ZINC (Zn) UNTUK APLIKASI MATERIAL IMPLAN ORTOPEDI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text COVER.pdf Download (1MB)
	Text BAB 1.pdf Download (392kB)
	Text BAB 2.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text BAB 4.pdf Restricted to Registered users only Download (2MB) | Request a copy
	Text BAB 5.pdf Restricted to Registered users only Download (384kB) | Request a copy
	Text DAFTAR PUSTAKA.pdf Download (507kB)
	Text LAMPIRAN.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

Penelitian ini membahas pengaruh penambahan magnesium (Mg) terhadap struktur mikro dan sifat mekanik logam Zinc (Zn) untuk aplikasi material implan ortopedi. Penelitian ini dilatarbelakangi oleh kebutuhan material implan biodegradable yang dapat terdegradasi secara alami dalam tubuh sehingga tidak memerlukan operasi kedua untuk pengangkatannya. Metode penelitian meliputi proses pengecoran dengan variasi komposisi Mg sebesar 0 wt%, 2 wt%, 3 wt%, dan 4 wt%, dilanjutkan dengan homogenisasi pada suhu 350 °C selama 5 jam. Hasil penelitian menunjukkan bahwa peningkatan kadar Mg memperhalus struktur mikro dan meningkatkan jumlah fasa eutektik (α-Zn + Mg₂Zn₁₁) di batas butir. Nilai kekerasan meningkat dari 29,26 VHN pada Zn murni menjadi 94,34 VHN pada Zn–4 Mg. Nilai kekuatan tarik (UTS) juga meningkat dari 30,43 MPa pada Zn murni menjadi 146 MPa pada paduan Zn–3 Mg, sebelum menurun menjadi 98,73 MPa pada 4 wt% Mg akibat terbentuknya fasa getas berlebih. Nilai elongasi mengalami penurunan, yaitu 1,03% pada Zn murni, menurun menjadi 0,44% pada Zn–2 Mg, kemudian menurun kembali pada Zn–3 Mg sebesar 0,32%, dan kemudian naik menjadi 0,49% pada Zn–4 Mg. Secara keseluruhan, penambahan Mg memberikan pengaruh signifikan terhadap peningkatan kekuatan dan kekerasan paduan Zn–Mg, sehingga material ini berpotensi digunakan sebagai implan biodegradable dengan keseimbangan kekuatan dan keuletan yang baik. Kata Kunci: Zinc (Zn), magnesium (Mg), struktur mikro, kekerasan, uji tarik, implan biodegradable. ***** This study investigates the effect of magnesium (Mg) addition on the microstructure and mechanical properties of Zinc (Zn) for orthopedic implant applications. The research is motivated by the need for biodegradable implant materials that can naturally degrade within the human body, eliminating the need for secondary surgery for removal. The experimental procedure involved casting with Mg composition variations of 0 wt%, 2 wt%, 3 wt%, and 4 wt%, followed by a homogenization process at 350 °C for 5 hours. The results show that increasing Mg content refines the microstructure and enhances the formation of the eutektik phase (α-Zn + Mg₂Zn₁₁) along the grain boundaries. The hardness value increased from 29.26 VHN for pure Zn to 94.34 VHN for Zn–4 Mg. The ultimate tensile strength (UTS) also increased from 30.43 MPa for pure Zn to 146 MPa for Zn–3 Mg, then decreased to 98.73 MPa at 4 wt% Mg due to the formation of excessive brittle intermetallic phases. The elongation value decreased, from 1.03% in pure Zn to 0.44% in Zn–2 Mg, then further decreased to 0.32% in Zn–3 Mg, and slightly increased to 0.49% in Zn–4 Mg. Overall, Mg addition significantly improves the strength and hardness of Zn–Mg alloys, making them promising candidates for biodegradable implant materials with a good balance of strength and ductility. Keywords: Zinc (Zn), magnesium (Mg), microstructure, hardness, tensile test, biodegradable implant.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Imam Basori, M.T. ; 2). Dr. Eng. Agung Premono, M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik
Divisions:	FT > S1 Teknik Mesin
Depositing User:	Radite Tedya Faizy .
Date Deposited:	23 Dec 2025 08:54
Last Modified:	23 Dec 2025 08:54
URI:	http://repository.unj.ac.id/id/eprint/62892

Actions (login required)

View Item