PENGARUH VARIASI KOMPOSISI SERABUT KELAPA PADA MATERIAL KOMPOSIT TERHADAP KEKERASAN, KEKASARAN PERMUKAAN, DAN STRUKTUR MIKRO

SYAHID QUDSI ALMUTAWAKKIL, . (2026) PENGARUH VARIASI KOMPOSISI SERABUT KELAPA PADA MATERIAL KOMPOSIT TERHADAP KEKERASAN, KEKASARAN PERMUKAAN, DAN STRUKTUR MIKRO. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 1. COVER.pdf Download (2MB)
	Text 2. BAB 1.pdf Download (539kB)
	Text 3. BAB 2.pdf Restricted to Registered users only Download (999kB) | Request a copy
	Text 4. BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text 5. BAB 4.pdf Restricted to Registered users only Download (968kB) | Request a copy
	Text 6. BAB 5.pdf Restricted to Registered users only Download (506kB) | Request a copy
	Text 7. DAFTAR PUSTAKA.pdf Download (492kB)
	Text 8. LAMPIRAN.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Penggunaan serabut kelapa sebagai penguat dalam komposit polimer bertujuan untuk meningkatkan nilai tambah limbah pertanian dan mendukung pengembangan material teknik yang berkelanjutan. Penelitian ini menganalisis pengaruh variasi komposisi serabut kelapa terhadap kekerasan, kekasaran permukaan, dan struktur mikro dari komposit yang menggunakan resin polyester. Variasi komposisi yang diuji adalah 40% serabut kelapa–60% resin polyester, 50%–50%, dan 60%–40%. Metode yang diterapkan meliputi proses cetakan tekan, kompaksi, dan sintering. Pengujian kekerasan dilakukan dengan durometer shore D, sedangkan kekasaran permukaan diukur menggunakan alat khusus, dan struktur mikro diamati dengan mikroskop optik. Hasil penelitian menunjukkan bahwa peningkatan persentase serabut kelapa mengakibatkan penurunan nilai kekerasan dan peningkatan kekasaran permukaan. Struktur mikro menunjukkan bahwa kandungan serabut yang lebih tinggi meningkatkan porositas dan ketidakmerataan ikatan antara serat dan matriks. Komposisi 40% serabut kelapa dan 60% resin poliester menunjukkan sifat mekanik dan struktur mikro yang optimal serta diharapkan menjadi referensi untuk pengembangan material komposit berbasis serat alami yang ramah lingkungan. ***** The use of coconut coir as a reinforcement in polymer composites aims to enhance the added value of agricultural waste and support the development of sustainable engineering materials. This study analyzes the effect of varying compositions of coconut coir on the hardness, surface roughness, and microstructure of composites using polyester resin. The tested composition variations include 40% coconut coir–60% polyester resin, 50%–50%, and 60%–40%. The methods employed include the processes of compression molding, compaction, and sintering. Hardness testing is conducted using a Shore D durometer, while surface roughness is measured with specialized equipment, and the microstructure is observed with an optical microscope. The results indicate that increasing the percentage of coconut coir leads to a decrease in hardness and an increase in surface roughness. The microstructure reveals that higher coir content results in increased porosity and uneven bonding between the fibers and the matrix. The composition of 40% coconut coir and 60% polyester resin shows optimal mechanical properties and microstructure, and it is expected to serve as a reference for the development of eco-friendly natural fiber-based composite materials.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ferry Budhi Susetyo, M.T., M.Si.; 2). Rani Anggrainy, S.Pd., M.T.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Syahid Qudsi Almutawakkil .
Date Deposited:	26 Jan 2026 02:05
Last Modified:	26 Jan 2026 02:05
URI:	http://repository.unj.ac.id/id/eprint/63648

Actions (login required)

View Item