PENGARUH DIAMETER LUBANG BARREL DALAM PROSES ELEKTROPLATING TEMBAGA PADA ALUMINIUM TERHADAP KETEBALAN LAPISAN, KEKERASAN, KEKASARAN, DAN KETAHANAN KOROSI

IDVI NUR UBAIDILLAH, . (2026) PENGARUH DIAMETER LUBANG BARREL DALAM PROSES ELEKTROPLATING TEMBAGA PADA ALUMINIUM TERHADAP KETEBALAN LAPISAN, KEKERASAN, KEKASARAN, DAN KETAHANAN KOROSI. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 1. COVER.pdf Download (1MB)
	Text 2. BAB 1.pdf Download (585kB)
	Text 3. BAB 2.pdf Restricted to Registered users only Download (570kB) | Request a copy
	Text 4. BAB 3.pdf Restricted to Registered users only Download (1MB) | Request a copy
	Text 5. BAB 4.pdf Restricted to Registered users only Download (611kB) | Request a copy
	Text 6. BAB 5.pdf Restricted to Registered users only Download (364kB) | Request a copy
	Text 7. DAFTAR PUSTAKA.pdf Download (338kB)
	Text 8. LAMPIRAN.pdf Restricted to Registered users only Download (3MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk menganalisis pengaruh variasi diameter lubang barrel terhadap karakteristik lapisan tembaga pada substrat aluminium melalui proses elektroplating metode barrel plating. Fokus utama penelitian ini adalah mengevaluasi bagaimana ukuran diameter lubang barrel memengaruhi kualitas fisik dan mekanis lapisan. Metode eksperimen dilakukan dengan variasi diameter lubang barrel sebesar 3, 4, dan 5 mm, menggunakan larutan elektrolit tembaga sulfat (CuSO4) selama waktu pelapisan 2 jam. Parameter yang diukur meliputi laju deposisi, ketebalan lapisan, kekerasan permukaan, kekasaran permukaan, serta ketahanan korosi. Hasil penelitian menunjukkan bahwa peningkatan diameter lubang barrel berbanding lurus dengan peningkatan laju deposisi dan ketebalan lapisan, di mana spesimen Cu-5 (lubang barrel 5 mm) menghasilkan ketebalan tertinggi sebesar 9.92 um. Nilai kekerasan tertinggi juga ditemukan pada spesimen Cu-5 sebesar 47,18 HV. Namun, diameter lubang yang lebih besar juga menyebabkan peningkatan kekasaran permukaan. Sebaliknya, spesimen Cu-3 (lubang barrel 3 mm) menunjukkan ketahanan korosi terbaik dengan laju korosi terendah sebesar 0,117 mm/tahun karena struktur lapisan yang lebih halus dan padat. Disimpulkan bahwa Semakin besar diameter lubang barrel yang digunakan maka laju deposisi dan ketebalan lapisan tembaga yang terbentuk akan meningkat, sehingga tingkat kekerasan permukaan juga ikut meningkat. Namun peningkatan laju deposisi yang telalu cepat dapat meningkatkan kekasaran permukaan dan berdampak pada laju korosi yang ikut meningkat. ***** This study aims to analyze the influence of barrel hole diameter variations on the characteristics of copper coatings on aluminum substrates using the barrel electroplating method. The primary focus of this research is to evaluate how the barrel hole size affects the physical and mechanical quality of the coating. The experimental method was conducted with barrel hole diameters of 3, 4, and 5 mm, utilizing a copper sulfate (CuSO4) electrolyte solution with a plating time of 2 hours. Measured parameters include deposition rate, coating thickness, surface hardness, surface roughness, and corrosion resistance. The results indicate that an increase in barrel hole diameter is directly proportional to the increase in deposition rate and coating thickness, where the Cu-5 specimen (5 mm hole) achieved the highest thickness of 9.92 µm. The highest hardness value was also found in the Cu-5 specimen at 47.18 HV. However, larger hole diameters also led to increased surface roughness. Conversely, the Cu-3 specimen (3 mm hole) demonstrated the best corrosion resistance with the lowest corrosion rate of 0.117 mm/year, due to a finer and denser coating structure. It is concluded that a larger barrel hole diameter increases the deposition rate and coating thickness, subsequently enhancing surface hardness. Nevertheless, an excessively rapid deposition rate can increase surface roughness, which in turn leads to a higher corrosion rate.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Dr. Ferry Budhi Susetyo, M.T., M.Si. ; 2). Ir. Yunita Sari, M.T., M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Teknologi (umum) Teknologi dan Ilmu Terapan > Teknologi (umum) > Teknologi Pendidikan Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Teknik Elektronika Teknologi dan Ilmu Terapan > Otomotif, Astronotika Teknologi dan Ilmu Terapan > Manufaktur Teknologi dan Ilmu Terapan > Ekonomi Rumahan
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	Idvi Nur Ubaidillah .
Date Deposited:	30 Jan 2026 02:59
Last Modified:	30 Jan 2026 02:59
URI:	http://repository.unj.ac.id/id/eprint/64503

Actions (login required)

View Item