PENGARUH VARIASI KECEPATAN PUTAR MESIN POLES TERHADAP HASIL KARAKTERISTIK TEKSTUR PERMUKAAN ALUMUNIUM 6061 DENGAN MENGGUNAKAN JIG HOLDER

ICHSAN ARFAN TIMUR, . (2026) PENGARUH VARIASI KECEPATAN PUTAR MESIN POLES TERHADAP HASIL KARAKTERISTIK TEKSTUR PERMUKAAN ALUMUNIUM 6061 DENGAN MENGGUNAKAN JIG HOLDER. Diploma thesis, UNIVERSITAS NEGERI JAKARTA.

	Text File COVER.pdf Download (1MB)
	Text File BAB 1.pdf Download (327kB)
	Text File BAB 2.pdf Restricted to Registered users only Download (450kB)
	Text File BAB 3.pdf Restricted to Registered users only Download (920kB)
	Text File BAB 4.pdf Restricted to Registered users only Download (1MB)
	Text File BAB 5.pdf Restricted to Registered users only Download (366kB)
	Text File DAFTAR PUSTAKA.pdf Download (293kB)
	Text File LAMPIRAN.pdf Restricted to Registered users only Download (1MB)

Abstract

Proses pemolesan merupakan tahap penting dalam metalografi untuk menghasilkan permukaan spesimen yang halus dan bebas goresan sebelum dilakukan pengukuran struktur mikro. Stabilitas selama proses pemolesan sangat dipengaruhi oleh kecepatan putaran mesin dan kinerja jig holder. Penelitian ini bertujuan untuk menganalisis pengaruh tiga variasi kecepatan putaran mesin yakni, sebesar 400, 500 dan 600 rpm dengan menggunakan jig holder terhadap karakteristik tekstur permukaan spesimen aluminium 6061. Penelitian dilakukan dengan menggunakan empat metode pendekatan yakni, melalui pengujian mikroskop optik, pengujian topografi permukaan, pengujian kekasaran permukaan dan pengujian korosi. Pendekatan utama berfokus pada nilai kekasaran permukaan dengan ketiga metode lainnya merupakan data pendukung. Hasil pengujian kekasaran menunjukkan bahwa peningkatan kecepatan putaran mesin menghasilkan penurunan nilai kekasaran permukaan. Spesimen pada kecepatan mesin 600 rpm menunjukkan nilai kekasaran rata-rata paling rendah sebesar 0,23 μm, lebih baik dibandingkan 500 rpm sebesar 0,42 μm dan 400 rpm sebesar 0,66 μm. Analisis mikroskop optik dan topografi permukaan memperkuat hasil tersebut, dimana distribusi nilai abu-abu pada kecepatan mesin 600 rpm menunjukkan histogram yang lebih stabil dan merata sebesar 160,03 gray value, lalu pada kecepatan 500 rpm sebesar 152,17 gray value dan terakhir spesimen dengan kecepatan 400 rpm sebesar 148,14 gray value. Pada hasil visualisasi 3D menunjukkan keseragaman goresan dengan persentasi nilai surface isotropy paling kecil yakni sebesar 8,30% pada kecepatan mesin 600 rpm, 8,60% pada kecepatan 500 rpm dan terakhir sebesar 12,65% pada kecepatan 400 rpm. Diikuti oleh nilai laju korosi, dengan menunjukkan kecepatan yang lebih tinggi menghasilkan nilai laju korosi yang lebih kecil yakni sebesar 0.0540563 mm⁄y. Dari keseluruhan hasil pengujian disimpulkan bahwa, kecepatan putaran mesin poles dengan menggunakan jig holder dapat mempengaruhi hasil permukaan spesimen alumunium 6061 secara signifikan. Kecepatan putar optimal yang memberikan kualitas permukaan terbaik adalah sebesar 600 rpm, dimana dapat menghasilkan nilai kekasaran yang lebih rendah, distribusi nilai abu-abu lebih stabil, dan kinerja jig holder yang lebih baik dalam menjaga hasil kualitas permukaan spesimen selama proses pemolesan berlangsung. Kata kunci: metalografi, pemolesan, jig holder, kecepatan putar, kekasaran, nilai keabuan, aluminium 6061 ***** The polishing process is a crucial step in metallography to produce a smooth, scratch-free specimen surface before microstructural measurements. Stability during the polishing process is significantly influenced by the machine's rotational speed and the performance of the jig holder. This study aims to analyze the effect of three variations in machine rotational speed: 400, 500, and 600 rpm, using a jig holder, on the surface characterization of 6061 aluminum specimens. The study was conducted using four approaches: optical microscopy, surface topography, surface roughness, and corrosion testing. The primary approach focused on surface roughness, with the third method providing supporting data. The roughness test results showed that increasing the machine's rotational speed resulted in a decrease in surface roughness. Specimens at 600 rpm showed the lowest average roughness value of 0.23 μm, compared to 0.42 μm at 500 rpm and 0.66 μm at 400 rpm. Optical microscopy and surface topography analysis confirmed these results, with a more stable and even distribution of grayscale values at 600 rpm, 152.17 at 500 rpm, and 148.14 at 400 rpm. 3D visualization revealed scratch uniformity, with the smallest surface isotropy percentage at 8.30% at 600 rpm, 8.60% at 500 rpm, and 12.65% at 400 rpm. This was followed by the corrosion rate, with higher speeds yielding a smaller corrosion rate of 0.0540563 mm⁄y. The overall measurement results concluded that the rotational speed of the pole machine using a jig holder significantly affected the surface finish of 6061 aluminum specimens. The optimal rotational speed that provides the best surface quality is 600 rpm, which can produce lower roughness values, more stable gray value distribution, and better jig holder performance in maintaining the surface quality of the specimen during the polishing process. Keywords: Metallography, Polishing, Jig holder, Rotational speed, Surface roughness, Grayscale value, Aluminum 6061

Item Type:	Thesis (Diploma)
Additional Information:	1). Ahmad Lubi, M.Pd., M.T. ; 2). Dr. Ferry Budhy Susetyo, M.T., M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > D IV Teknologi Rekayasa Manufaktur
Depositing User:	Users 33099 not found.
Date Deposited:	11 Feb 2026 07:11
Last Modified:	11 Feb 2026 07:11
URI:	http://repository.unj.ac.id/id/eprint/65261

Actions (login required)

View Item