PENGARUH KECEPATAN PUTAR DAN KEDALAMAN POTONG TERHADAP TINGKAT KEKASARAN PERMUKAAN HASIL PEMBUBUTAN BAJA ST 37

JOHN PHILIP TAMPUBOLON, . (2025) PENGARUH KECEPATAN PUTAR DAN KEDALAMAN POTONG TERHADAP TINGKAT KEKASARAN PERMUKAAN HASIL PEMBUBUTAN BAJA ST 37. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text Cover.pdf Download (869kB)
	Text BAB 1.pdf Download (292kB)
	Text BAB 2.pdf Restricted to Registered users only Download (590kB)
	Text BAB 3.pdf Restricted to Registered users only Download (357kB)
	Text BAB 4.pdf Restricted to Registered users only Download (391kB)
	Text BAB 5.pdf Restricted to Registered users only Download (260kB)
	Text Daftar Pustaka.pdf Download (273kB)
	Text Lampiran.pdf Restricted to Registered users only Download (1MB)

Abstract

Proses pembubutan memainkan peran krusial dalam industri manufaktur untuk memproduksi barang. Kualitas produk sangat dipengaruhi oleh kualitas proses pembubutan, yang terlihat dari segi bentuk, presisi ukuran, dan tingkat kekasaran permukaan yang rendah. Kekasaran permukaan dari benda yang dihasilkan bergantung pada pemilihan parameter pemotongan yang tepat. Untuk memperoleh nilai kekasaran permukaan yang baik, sesuai dengan standar ISO 1302, dalam rentang 0,8-1,6µm, diperlukan penelitian mengenai dampak kecepatan putar dan kedalaman potong terhadap tingkat kekasaran permukaan pada pembubutan baja ST 37. Dalam penelitian ini, material yang digunakan sebagai sampel adalah baja ST 37. Proses pembubutan dilakukan dengan mesin bubut konvensional C6240A dan pahat HSS Bohler, serta menggunakan cairan pendingin berupa coolant semi- sintetik. Variasi parameter pemotongan yang diterapkan meliputi kecepatan potong 70 m/menit dan 90 m/menit, serta kedalaman pemotongan (depth of cut) sebesar 0,25 mm, 0,55 mm, dan 0,75 mm. Kecepatan putar spindle yang digunakan adalah 560 rpm, 800 rpm, dan 1120 rpm. Selanjutnya, pengujian kekasaran permukaan pada sampel baja ST 37 yang telah dibubut dilakukan dengan menggunakan Mitutoyo Surfest SJ-301. Hasil penelitian menunjukkan bahwa setelah melakukan variasi pada parameter pemotongan, baik kecepatan putar spindle maupun kedalaman potong, nilai kekasaran permukaan terendah ditemukan pada sampel dengan kecepatan potong 90 m/menit, kedalaman pemakanan 0,25 mm, dan kecepatan putar spindle 1120 rpm, yang menghasilkan nilai kekasaran sebesar 2,82µm. Kata Kunci : Baja ST 37, cutting speed, depth of cut. ***** The turning process plays a crucial role in the manufacturing industry for producing goods. Product quality is significantly influenced by the quality of the turning process, which is reflected in terms of shape, size precision, and low surface roughness. The surface roughness of the produced workpiece depends on the selection of appropriate cutting parameters. To achieve a good surface roughness value, in accordance with ISO 1302 standards, within the range of 0.8-1.6µm, research is needed on the impact of spindle speed and depth of cut on surface roughness levels in turning ST 37 steel. In this study, the material used as a sample is ST 37 steel. The turning process was conducted using a conventional lathe C6240A and HSS Bohler cutting tools, along with a semi-synthetic coolant. The variations in cutting parameters applied include cutting speeds of 70 m/min and 90 m/min, as well as depth of cut values of 0.25 mm, 0.55 mm, and 0.75 mm. The spindle speeds used were 560 rpm, 800 rpm, and 1120 rpm. Furthermore, surface roughness testing on the turned ST 37 steel samples was carried out using the Mitutoyo Surfest SJ-301. The results of the study indicate that after varying the cutting parameters, both spindle speed and depth of cut, the lowest surface roughness value was found in the sample with a cutting speed of 90 m/min, a depth of cut of 0,25 mm, and a spindle speed of 1120 rpm, resulting in a surface roughness value of 2.82µm. Keywords: spindle speed, depth of cut, ST 37 steel.

Item Type:	Thesis (Sarjana)
Additional Information:	1). Drs. Syaripuddin, M.Pd. ; 2). Dr. Ferry Budhi Susetyo, M.T., M.Si.
Subjects:	Teknologi dan Ilmu Terapan > Teknik Mesin, Mekanika Teknik Teknologi dan Ilmu Terapan > Manufaktur
Divisions:	FT > S1 Pendidikan Teknik Mesin
Depositing User:	John Philip Tampubolon .
Date Deposited:	03 Feb 2026 02:58
Last Modified:	03 Feb 2026 02:58
URI:	http://repository.unj.ac.id/id/eprint/64727

Actions (login required)

View Item