PEMANFAATAN ABU KULIT KERANG SEBAGAI SUBSTITUSI SEBAGIAN SEMEN DENGAN PENAMBAHAN FOAM AGENT TERHADAP KARAKTERISTIK BETON RINGAN NON STRUKTURAL

RIANTO, . (2015) PEMANFAATAN ABU KULIT KERANG SEBAGAI SUBSTITUSI SEBAGIAN SEMEN DENGAN PENAMBAHAN FOAM AGENT TERHADAP KARAKTERISTIK BETON RINGAN NON STRUKTURAL. Sarjana thesis, UNIVERSITAS NEGERI JAKARTA.

	Text 5. LEMBAR PENGESAHAN.doc Download (0B)
	Text 4. ABSTRACT.doc Download (31kB)
	Text 1. COVER.doc Download (43kB)
	Text 2. HALAMAN JUDUL.doc Download (44kB)
	Text 3. ABSTRAK.doc Download (32kB)
	Text 7. KATA PENGANTAR.doc Download (56kB)
	Text 8. DAFTAR ISI.docx Download (30kB)
	Text 6. HALAMAN PERNYATAAN.doc Download (381kB)
	Text 11. DAFTAR LAMPIRAN.doc Download (51kB)
	Text 10. DAFTAR GAMBAR.doc Download (51kB)
	Text 9. DAFTAR TABEL.doc Download (51kB)
	Text BAB III.docx Download (92kB)
	Text BAB II.docx Download (79kB)
	Text BAB I.doc Download (50kB)
	Text BAB IV.docx Download (260kB)
	Text BAB V.docx Download (22kB)
	Text DAFTAR PUSTAKA.docx Download (22kB)
	Text DAFTAR RIWAYAT HIDUP.docx Download (226kB)

Abstract

Beton ringan non struktural ini terbuat dari pasir, semen, foam agent dan abu kulit kerang sebagai substitusi sebagian semen. Penelitian ini bertujuan untuk mengetahui penambahan abu kulit kerang terhadap nilai kuat tekan dan kuat lentur dengan variasi 0%, 5%, 7,5% dan 10% untuk rancangan mutu beton 1,4 MPa. Penelitian ini dilaksanakan di Laboratorium Biokomposit, Pusat Penelitian Biomaterial, Lembaga Ilmu Pengetahuan Indonesia (LIPI) dengan metode eksperimen. Benda uji yang digunakan yaitu silinder dengan diameter 3 inch dan tinggi 6 inch untuk kuat tekan dan diuji menggunakan alat Compression Testing Machine (CTM). Untuk pengujian kuat lentur digunakan benda uji berupa balok dengan panjang 16 cm, lebar 4 cm dan tinggi 4 cm dan diuji menggunakan alat Universal Testing Machine (UTM). Hasil penelitian menunjukkan bahwa terdapat perbedaan pada beton normal dan beton dengan penambahan abu kulit kerang. Kuat tekan dan kuat lentur optimum pada umur 28 hari terjadi pada variasi penambahan abu kulit kerang sebesar 7.5% yaitu 1,54 MPa dan 0,95 MPa. Penggunaan abu kulit kerang sebagai substitusi sebagian semen dapat meningkatkan kekuatan beton ringan, namun semakin tinggi kadar abu kulit kerang akan semakin memperkecil kekuatan beton. Hal ini disebabkan karena kandungan tertinggi abu kulit kerang yaitu kalsium oksida hanya sebagai accelerating admixture atau mempercepat waktu pengikatan. Non-structural lightweight concrete is made from sand, cement, foam agent and ash shells as partial substitution of cement. This study aims to determine the ash addition of seashells on the compressive strength and flexural strength with a variation of 0%, 5%, 7.5% and 10% for the design of concrete quality 1.4 MPa. This research was conducted at the Laboratory of biocomposite, Biomaterial Research Center, Indonesian Institute of Science (LIPI) with the experimental method. The test specimen used is a cylinder with a diameter of 3 inches and 6 inches high and tested for compressive strength using tools Compression Testing Machine (CTM). For the flexural strength test specimen used in the form of beams with a length of 16 cm, 4 cm wide and 4 cm high and tested using a Universal Testing Machine (UTM). The results showed that there were differences in normal concrete and concrete with the addition of ash shells. Compressive strength and flexural strength optimum at 28 days occurred on addition of ash shells variation of 7.5% which is 1.54 MPa and 0.95 MPa. The use of ash shells as partial substitution of cement can increase the strength of lightweight concrete, but the higher ash content will be further reduced shells of concrete strength. This is because the high ash content of calcium oxide shells are just as accelerating admixture or accelerate the bonding time.

Item Type:	Thesis (Sarjana)
Additional Information:	1) Dra. Nira Nasution, S.T., M.Pd 2) Ismail Budiman, S.Hut, M.Si
Subjects:	Teknologi dan Ilmu Terapan > Teknik Sipil
Divisions:	FT > S1 Pendidikan Teknik Bangunan
Depositing User:	sawung yudo
Date Deposited:	27 Apr 2022 01:41
Last Modified:	27 Apr 2022 01:41
URI:	http://repository.unj.ac.id/id/eprint/28273

Actions (login required)

View Item